DownloadProducts
HOME > Silicone
LSR Additional curing type mould-making silicone rubber
LIQUID SILICONE RUBBER
Catalyst type: Platinum (PT) type
Mix rate: 10:1
Appearance: Liquid
Hardness: 27 Shore A
Curing temperature: at room temperature & heating temperature
Storage life: 24 months
Package: 1kg, 5kgs, 20kgs, 200kgs
Product description
LSR-1527 is two components additional curing type mould-making silicone rubber. It is cured with Platinum (PT) type catalyst & mix rate is 10:1. It is non-poisonous & no smell. It can be cured at room temperature & heating temperature both. It has extraordinary properties, as low linear shrinkage, high transparency, high tear resistance, high tensile resistance, high temperature resistance (limit 300℃) & long lifetime etc. It is a new & popular technology product applied widely in all trades & industries.
Application:
LSR-1527 is applied in making exquisite article mould. It can be used for epoxy resin, button, artificial jewelry, exquisite handmade article mould & cement-gypsum mould, etc.
Also it is up to food grade. It can be applied in making food moulds, as chocolate mould, cookies mould, candy mould, pie mould & cake mould etc.
Technology data sheet:
|
Item No. |
LSR-1527 |
LSR-1520 |
LSR-1530 |
LSR-1535 |
LSR-1540 |
|
|
Color |
Component A |
Transparent |
Transparent |
Transparent |
Transparent |
Transparent |
|
Component B |
Transparent |
Transparent |
Transparent |
Transparent |
Transparent |
|
|
Viscosity (25℃ mPa.s) |
Component A |
90,000 ±5,000 |
90,000 ±5,000 |
90,000 ±5,000 |
90,000 ±5,000 |
90,000 ±5,000 |
|
Component B |
350±50 |
350±50 |
350±50 |
350±50 |
350±50 |
|
|
Consistency (25℃) g/ cm3 |
1.1 |
1.1 |
1.1 |
1.1 |
1.1 |
|
|
Gel Time (hour) |
2~3 |
2~3 |
2~3 |
2~3 |
2~3 |
|
|
Mix Rate |
10:1 |
10:1 |
10:1 |
10:1 |
10:1 |
|
|
Curing Condition (℃/ time) |
Room Temperature (25 ℃) |
12 hours |
12 hours |
12 hours |
12 hours |
12 hours |
|
Heating Temperature℃
|
NO |
NO |
NO |
NO |
NO |
|
|
Heating Temperature℃
|
150℃/ 1min |
150℃/ 1min |
150℃/ 1min |
150℃/ 1min |
150℃/ 1min |
|
|
Hardness (Shore A) |
27 |
20 |
30 |
35 |
40 |
|
|
Tear Strength (N/ mm) |
13±1 |
13±1 |
13±1 |
12±1 |
12±1 |
|
|
Tensile Strength (MPa) |
4±1 |
4±1 |
4±1 |
4±1 |
4±1 |
|
|
Elongation At Break (%) |
450 |
450 |
450 |
400 |
350 |
|